Author Topic: Al vs. SS. Which Heats Faster?  (Read 4424 times)

Offline hopfenundmalz

  • Global Moderator
  • I must live here
  • *****
  • Posts: 10678
  • Milford, MI
Al vs. SS. Which Heats Faster?
« on: November 22, 2010, 05:31:47 pm »
AL vs. SS myths, time for an experiment.

AL can be used for a boil kettle.  No it is ok if seasoned.  Busted.
AL causes Alzheimers.  This has been Busted by scientific research.
AL will heat the wort faster due to the higher conductivity of the AL over SS.   Well how much faster?

The overall heat transfer coefficient is what is important for a system.   The system I use is a propane burner, the pot then the wort, so there are 3 heat conductors in series.  People on the internet always say that AL will be faster due to the much higher conductivity.  If you look on the web you will find the following for AL, and SS.

AL =  250 (W/m-degree C)
SS = 16  (W/m-degree C)

So the AL has greater than an order of magnitude of  advantage in heat transfer per unit thickness

So to see how much time I was wasting on a brew day, I was able to do a quick test, since we recently were given a  AL pot that as very close to a ss one we had.  These are both about 10 quarts, and are very close in diameter and height, you have to get them side by side to see that the AL one is about ¼ inch taller.  I thought there would be a small advantage to the AL, for what it is worth, but not enough to worry about.

Both pots were filled with 2 gallons of water.   The Aluminum pot was put on first, and the temp was measured with a digital thermometer.  Started  the time at 110F, since my brother called and interrupted,  and went to 200F, just because I was heating some of the sparge water.  The AL was taken off and the SS was put on, and the propane valve was not adjusted (30 pounds in a 40 pound tank, so it was running steady).  Both were uncovered.   So what was the time?

AL = 15 min. 55 seconds
SS = 15 min. 20 seconds

Whoa!  What the heck? 

One clue is that the digital thermometer was jumping 3 to 4 degrees +/- with the AL pot vs. about 1 degree with the SS pot.  The AL pot was even stirred several time while trying to take a steady reading, which should have helped its convection heat transfer.  My guess it that the AL pot had higher convection currents out the sides   These pots are as high as they are in diameter, so when you do the math, there is 4 times the surface are on the sides than on the bottom.  The AL can transfer heat to the wort better in the bottom, but it can lose it faster through the sides.

This is far from a conclusive test, but when someone on a random website says my AL kettle will be faster, I will not lose any sleep.  I have some bigger SS and AL pots to try. 

AL is faster - Busted?  More heating experiments are in order.  If you have any data to share, please do.  Or just flame me if you want.   ;D




Jeff Rankert
AHA Lifetime Member
BJCP National
Ann Arbor Brewers Guild
Home-brewing, not just a hobby, it is a lifestyle!

Offline tubercle

  • Senior Brewmaster
  • ******
  • Posts: 1639
  • Sweet Caroline
Re: Al vs. SS. Which Heats Faster?
« Reply #1 on: November 22, 2010, 06:31:23 pm »
  The AL can transfer heat to the wort better in the bottom, but it can lose it faster through the sides.

 Might be that. Conduction is a two way street.
Sweet Caroline where the Sun rises over the deep blue sea and sets somewhere beyond Tennessee

Offline tschmidlin

  • I must live here
  • **********
  • Posts: 8198
  • Redmond, WA
Re: Al vs. SS. Which Heats Faster?
« Reply #2 on: November 23, 2010, 12:01:36 am »
What are the thicknesses of the bottom of the two different kettles?  Do you know?

I like your hypothesis that the Al kettle will lose heat faster through the sides than the SS kettle, I hadn't thought of that before.
Tom Schmidlin

Offline geobrewer

  • Cellarman
  • **
  • Posts: 28
    • GeoBrewer
Re: Al vs. SS. Which Heats Faster?
« Reply #3 on: November 23, 2010, 05:41:27 am »
What are the thicknesses of the bottom of the two different kettles?  Do you know?

...and, does the SS kettle have a 3 ply bottom? Aluminum layer sandwiched between 2 SS layers?

Offline hopfenundmalz

  • Global Moderator
  • I must live here
  • *****
  • Posts: 10678
  • Milford, MI
Re: Al vs. SS. Which Heats Faster?
« Reply #4 on: November 23, 2010, 06:05:35 am »
Both pots were single layer.  The SS was not so thick.  The AL was not all that thick either. 

There are some clad SS pots in the kitchen, maybe I should take one to the garage for the next round.
Jeff Rankert
AHA Lifetime Member
BJCP National
Ann Arbor Brewers Guild
Home-brewing, not just a hobby, it is a lifestyle!

Offline richardt

  • Senior Brewmaster
  • ******
  • Posts: 1227
Re: Al vs. SS. Which Heats Faster?
« Reply #5 on: November 23, 2010, 06:53:06 am »
I think that would be interesting to see if a tri-clad (SS-Al-SS) bottomed SS kettle is just as fast, or even faster (due to less heat loss out the sides).

Offline abraxas

  • Assistant Brewer
  • ***
  • Posts: 191
Re: Al vs. SS. Which Heats Faster?
« Reply #6 on: November 23, 2010, 07:09:03 am »
I work in industrial heat processing.  I asked our Phd R&D manager who works in a lab testing out and simulating heat transfer scenarios and he said his gut told him SS pot of similar thickness would heat up a set amount of water to a boil quicker due to greater wall losses in the aluminum pot.

Offline hopfenundmalz

  • Global Moderator
  • I must live here
  • *****
  • Posts: 10678
  • Milford, MI
Re: Al vs. SS. Which Heats Faster?
« Reply #7 on: November 23, 2010, 07:38:44 am »
I work in industrial heat processing.  I asked our Phd R&D manager who works in a lab testing out and simulating heat transfer scenarios and he said his gut told him SS pot of similar thickness would heat up a set amount of water to a boil quicker due to greater wall losses in the aluminum pot.

Thanks for asking.  In my engineering specialty (N&V), you often have to account for all of the energy flow, so that is how I came to my guess.
Jeff Rankert
AHA Lifetime Member
BJCP National
Ann Arbor Brewers Guild
Home-brewing, not just a hobby, it is a lifestyle!

Offline a10t2

  • Official Poobah of No Life. (I Got Ban Hammered by Drew)
  • *********
  • Posts: 4696
  • Ask me why I don't like Chico!
    • SeanTerrill.com
Re: Al vs. SS. Which Heats Faster?
« Reply #8 on: November 23, 2010, 08:41:14 am »
The overall heat transfer coefficient is what is important for a system.

That's true, but the constants you listed aren't the heat transfer coefficients (h), they're the thermal conductivities (k). The thermal conductivity of any metal is massive relative to the fluids on either side (air and water in this case), so either kettle would be very nearly the same temperature on the top and the bottom. Moreover, the layer of metal is very thin (note that the units for k are meters). For an 18-gauge (1.27 mm) layer of metal with air on one side and water on the other, the heat transfer coefficients would be:

hAl = 43.3908 W/m2-K
hSS = 43.3909 W/m2-K

with the extra digits added for emphasis. I'd expect no detectable difference in their performance.
Sent from my Microsoft Bob

Beer is like porn. You can buy it, but it's more fun to make your own.
Refractometer Calculator | Batch Sparging Calculator | Two Mile Brewing Co.

Offline hopfenundmalz

  • Global Moderator
  • I must live here
  • *****
  • Posts: 10678
  • Milford, MI
Re: Al vs. SS. Which Heats Faster?
« Reply #9 on: November 23, 2010, 09:28:59 am »
My heat transfer course was a long long time ago.  Nixon was President. 

Yes, I listed the conductivity, just the lazy look up. 

So if 1/Heq=1/H(air) + 1/H(metal)+1/H(liquid), I do remember that the liquid and especially the air(well the fire) side will control the heat transfer.   

The expected result was that the SS would be about the same as the AL, maybe slighlty longer.  Faster was not expected for the SS.  But once again, the energy flow has to be accounted for in the system.

Jeff Rankert
AHA Lifetime Member
BJCP National
Ann Arbor Brewers Guild
Home-brewing, not just a hobby, it is a lifestyle!

Offline BrewArk

  • Brewmaster
  • *****
  • Posts: 575
  • Rick - Newark, California
    • BrewArk
Re: Al vs. SS. Which Heats Faster?
« Reply #10 on: November 23, 2010, 09:59:51 am »
Then there's the question of which is better after you reach boiling.  If stainless doesn't conduct heat out of the system as easily as aluminum, it could maintain the boil w/less energy input after you reach equilibrium?
Beer...Now there's a temporary solution!

Na Zdraví

Offline hopfenundmalz

  • Global Moderator
  • I must live here
  • *****
  • Posts: 10678
  • Milford, MI
Re: Al vs. SS. Which Heats Faster?
« Reply #11 on: November 23, 2010, 10:13:39 am »
Then there's the question of which is better after you reach boiling.  If stainless doesn't conduct heat out of the system as easily as aluminum, it could maintain the boil w/less energy input after you reach equilibrium?

Yes, that is probably true.

I will have to look closer at the Peter Ausin system at one of the local brewpubs.  If the boil kettle is all copper, it would help explain why the sides have a brick vener.
Jeff Rankert
AHA Lifetime Member
BJCP National
Ann Arbor Brewers Guild
Home-brewing, not just a hobby, it is a lifestyle!

Offline richardt

  • Senior Brewmaster
  • ******
  • Posts: 1227
Re: Al vs. SS. Which Heats Faster?
« Reply #12 on: November 23, 2010, 10:39:32 am »
Then there's the question of which is better after you reach boiling.  If stainless doesn't conduct heat out of the system as easily as aluminum, it could maintain the boil w/less energy input after you reach equilibrium?

Yes, that is probably true.

I will have to look closer at the Peter Ausin system at one of the local brewpubs.  If the boil kettle is all copper, it would help explain why the sides have a brick vener.

If direct fired, perhaps you'd see a fire-proof liner (e.g., made of asbestos, or modern equivalent) between the vessel and the brick veneer.
Another possibility is that the brick veneer conceals the steam jacketed vessels.

Offline mabrungard

  • I spend way too much time on the AHA forum
  • ********
  • Posts: 2902
  • Water matters!
    • Bru'n Water
Re: Al vs. SS. Which Heats Faster?
« Reply #13 on: November 23, 2010, 10:46:02 am »
Very interesting problem.  I had not thought about the heat losses through the sides of the kettle, but they are obvious.  Insulating the kettle sides can be difficult if you're dealing with a direct-fired kettle as most homebrewers do.  

Off hand, I'd say that fabricating a metal skirt with a circumference about the size of the outer diameter of the pot lip might be a good energy saving enhancement.  The skirt length would be about the same as the pot height.  I'd say that if you formed the top of the skirt to sit on the lip of the pot without gaps, you would create an somewhat insulated air-space between the pot and the skirt down the pot sides.  That would provide some insulation to heat loss through the sides.  

A better option would probably be to insulate the pot sides with another material, but I'm having difficulty thinking of a fire and water resistant material that could be wrapped around a pot.  It would need to be relatively durable.  Maybe that stiff fiberglass sheeting with the metal foil that they use to create HVAC ducts?  Maybe it could just be banded onto the pot somehow?

The same argument for heat loss through the sides can be applied to the lid of your pot.  I partially cover during the boil to reduce heat losses.  That could be further insulated too.

Any other ideas?


Martin B
Carmel, IN

BJCP National
Foam Blowers of Indiana (FBI)

Brewing Water Information at:
https://www.brunwater.com/

Like Bru'n Water on Facebook
https://www.facebook.com/Brun-Water-464551136933908/?ref=bookmarks

Offline a10t2

  • Official Poobah of No Life. (I Got Ban Hammered by Drew)
  • *********
  • Posts: 4696
  • Ask me why I don't like Chico!
    • SeanTerrill.com
Re: Al vs. SS. Which Heats Faster?
« Reply #14 on: November 23, 2010, 10:56:28 am »
Then there's the question of which is better after you reach boiling.  If stainless doesn't conduct heat out of the system as easily as aluminum, it could maintain the boil w/less energy input after you reach equilibrium?

For a given geometry, the conductivities would be essentially identical. Even if the walls were one inch thick, the difference is 0.003%.
Sent from my Microsoft Bob

Beer is like porn. You can buy it, but it's more fun to make your own.
Refractometer Calculator | Batch Sparging Calculator | Two Mile Brewing Co.